| GB | JIS | UNS | W.Nr | ||||
| — | — | N04401 | — | ||||
| Executive standard | （ASTM）（ASME）（AMS）（JIS）（DIN）（GB） | ||||||
| Surface: | Mill;HL;Polish;Mirror;NO.4;Pvd….. | ||||||
| Tchnology: | Solution Treatment；Annealing | ||||||
| MOQ: | 200KG | ||||||
| Payment Term: | T/T;L/C;WesternUnion;Paypal | ||||||
| Delivery Time: | 7-15days upon receipt of the deposit | ||||||
| Package: | Standard Expot Packing or As Customers Requirement | ||||||
| Processing form：
|
 |
 |
 |
 |
 |
||
Monel alloy 401 Material
Product Description:
Product Details：Monel alloy401 coil; Monel alloy 401 strip
Monel alloy 401 plate; Monel alloy 401 sheets;
Monel alloy 401 tube; Monel alloy 401 pipe;
Monel alloy 401 flat; Monel alloy 401 bar
Stainless Steel Details
Chemical composition
| C | Si | Mn | Cu | S | Ni | Fe | Al |
| ≤
0.10 |
≤
0.25 |
≤
2.25 |
balance | ≤
0.024 |
40.00-
45.00 |
≤
0.75 |
≤
0.05 |
Mechanical Property
| T.S(Mpa)≥ | YS(Mpa)≥ | EL(%)≥ | HB |
| 441 | 134 | 35 | — |
Chemical composition
| C | Si | Mn | Cu | S | Ni | Fe | Al |
| ≤
0.10 |
≤
0.25 |
≤
2.25 |
balance | ≤
0.024 |
40.00-
45.00 |
≤
0.75 |
≤
0.05 |
Mechanical Property
| T.S(Mpa)≥ | YS(Mpa)≥ | EL(%)≥ | HB |
| 441 | 134 | 35 | — |
Stainless Steel Introduce
Monel 401 has excellent strength and plasticity, and has good pressure processing performance in both cold and hot states. It is a corrosion-resistant alloy with large dosage, wide application and excellent comprehensive performance. The alloy has excellent corrosion resistance in HF and F2 media, and is one of the few important materials that can withstand hydrofluoric acid. An important feature of this alloy is that it generally does not produce stress corrosion cracks and has good cutting performance. A kind of Monel alloy, its alloy structure is a high-strength single-phase solid solution, 3 a nickel-based alloy similar to Monel 400, and the corrosion resistance of the metal is fundamentally obtained by hindering the migration of charged particles through the discharge process of hydrogen ions. Obtained, the addition of 30% Cu by mass fraction minimizes the corrosion rate of TH, Ni in F, Cl and other halogen element ionic media, and the higher the Cu content, the better the resistance to sulfuric acid and phosphoric acid. Adding mass fraction to Monel 401 55% Cu improves the corrosion resistance of the alloy in reducing acids.
Application fields
Wirewound Resistors
bimetal contact
Electrical and Electronic Applications
Marine Engineering
Chemical and Hydrocarbon Processing Equipment
petrol and fresh water tanks
Distiller
degas heater
Boiler feed water heaters and other heat exchangers
Valves, pumps, shafts, fittings and fasteners
Industrial heat exchanger
Chlorinated solvents
Crude distillation tower
Wirewound Resistors
bimetal contact
Electrical and Electronic Applications
Marine Engineering
Chemical and Hydrocarbon Processing Equipment
petrol and fresh water tanks
Distiller
degas heater
Boiler feed water heaters and other heat exchangers
Valves, pumps, shafts, fittings and fasteners
Industrial heat exchanger
Chlorinated solvents
Crude distillation tower